Home Welding Products Brazing 0 Phos-Copper Brazing Alloy .050 x 1/8" x 28 Stick Tube

Harris Products Group

0 Phos-Copper Brazing Alloy .050 x 1/8" x 28 Stick Tube

PART 0
MFG 0620F1
Calculating price...
QUANTITY

About this item

  • Economical choice for copper brazing
  • Copper is self-fluxing
  • Alloy flows quickly at brazing temperature so requires close joint tolerance
  • Used in manual brazing applications
  • Suitable for brazing brass
  • Operators should avoid over heating the brass and use STAY-SILV® white brazing flux
  • Not recommended for brazing steel or other ferrous base metals
  • Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including HARRIS® 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service
  • Recommended joint clearance of 0.002" - 0.007" (0.05mm - 0.18mm)
  • Conforms to the EU Reach & RoHS directive
Specification Sheet
Specification Sheet
Catalog
Catalog
SDS
SDS
Brand Harris Products Group
Diameter .050" x 1/8" (1.27mm x 3.18mm)
Length 20 in
Temperature Rating 1310 deg F, 1460 deg F
Composition 92 to 94% Copper, 6 to 8% Phosphorus
ModelName HARRIS® 0
Electrical Conductivity (%IACS) 9.9
Electrical Resistivity (Microhm/Cm) 19.2
Liquidus 1460 deg F (793 deg C)
Size 28 stick tube
Fluidity Rating 5
Alloy Type PhosCopper
Solidus 1310 deg F (710 deg C)
Chemical Composition Copper Remainder%
Brazing Temperature Range 1345 deg F-1500 deg F (729 deg C-816 deg C)
Recommended Joint Clearance .002"-.007" (.051mm-.178mm)
Recommended Flux No flux required for copper brazing. For brazing brass or copper to brass use Stay-Silv white flux. When flux is required, Harris Eco Smart boric acid free flux (powder or paste) is an excellent choice to promote sound brazed assemblies and comply with European REACH requirements.